Ceramic primer heat-treatment effect on resin cement/Y-TZP bond strength.

The purpose of this study was to evaluate the effect of different heat-treatment strategies for a ceramic primer on the shear bond strength of a 10-methacryloyloxydecyl-dihydrogen-phosphate (MDP)-based resin cement to a yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic. Specimens measuring 4.5 × 3.5 × 4.5 mm(3) were produced from Y-TZP presintered cubes and embedded in polymethyl methacrylate (PMMA). Following finishing, the specimens were cleaned using an ultrasound device and distilled water and randomly divided into 10 experimental groups (n=14) according to the heat treatment of the ceramic primer and aging condition. The strategies used for the experimental groups were: GC (control), without primer; G20, primer application at ambient temperature (20°C); G45, primer application + heat treatment at 45°C; G79, primer application + heat treatment at 79°C; and G100, primer application + heat treatment at 100°C. The specimens from the aging groups were submitted to thermal cycling (6000 cycles, 5°C/55°C, 30 seconds per bath) after 24 hours. A cylinder of MDP-based resin cement (2.4 mm in diameter) was constructed on the ceramic surface of the specimens of each experimental group and stored for 24 hours at 37°C. The specimens were submitted to a shear bond strength test (n=14). Thermal gravimetric analysis was performed on the ceramic primer. The data obtained were statistically analyzed by two-way analysis of variance and the Tukey test (α=0.05). The experimental group G79 without aging (7.23 ± 2.87 MPa) presented a significantly higher mean than the other experimental groups without aging (GC: 2.81 ± 1.5 MPa; G20: 3.38 ± 2.21 MPa; G100: 3.96 ± 1.57 MPa), showing no difference from G45 only (G45: 6 ± 3.63 MPa). All specimens of the aging groups debonded during thermocycling and were considered to present zero bond strength for the statistical analyses. In conclusion, heat treatment of the metal/zirconia primer improved bond strength under the initial condition but did not promote stable bonding under the aging condition.

Influence of acid-etching and ceramic primers on the repair of a glass ceramic.

The objective of this study was to evaluate the influence of different primers on the microtensile bond strength (µTBS) between a feldspathic ceramic and two composites. Forty blocks (6.0 x 6.0 x 5.0 mm³) were prepared from Vita Mark II . After polishing, they were randomly divided into 10 groups according to the surface treatment: Group 1, hydrofluoric acid 10% (HF) + silane; Group 2, CoJet + silane; Group 3, HF + Metal/Zirconia Primer; Group 4, HF + Clearfil Primer; Group 5, HF + Alloy Primer; Group 6, HF + V-Primer; Group 7, Metal/Zirconia Primer; Group 8, Clearfil Primer; Group 9, Alloy Primer; Group 10, V-Primer. After each surface treatment, an adhesive was applied and one of two composite resins was incrementally built up. The sticks obtained from each block (bonded area: 1.0 mm² ± 0.2 mm) were stored in distilled water at 37 degrees C for 30 days and submitted to thermocycling (7,000 cycles; 5 degrees C/55 degrees C ± 1 degree C). The µTBS test was carried out using a universal testing machine (1.0 mm/min). Data were analyzed using ANOVA and a Tukey test (a = 0.05). The surface treatments significantly affected the results (P < 0.05); no difference was observed between the composites (P > 0.05). The bond strength means (MPa) were as follows: Group 1a = 29.6; Group 1b = 33.7; Group 2a = 28.9; Group 2b = 27.1; Group 3a = 13.8; Group 3b = 14.9; Group 4a = 18.6; Group 4b = 19.4; Group 5a = 15.3; Group 5b = 16.5; Group 6a = 11; Group 6b = 18; Groups 7a to 10b = 0. While the use of primers alone was not sufficient for adequate bond strengths to feldspathic ceramic, HF etching followed by any silane delivered higher bond strength.

Diversidade genética de estoques de reprodutores de Colossoma macropomum / Genetic diversity of Colossoma macropomum broodstocks

Analisou-se a diversidade genética de estoques de reprodutores de Tambaqui (Colossoma macropomum), mediante o uso de marcador RAPD, utilizando-se 10 primers para analisar 30 amostras do estoques de reprodutores das pisciculturas de Boa Esperança e Vale Verde, localizadas no Estado de Rondônia. A porcentagem de fragmentos polimórficos e o índice de diversidade genética de Shannon foram altos nos dois estoques de reprodutores. O estoque de reprodutores de Boa Esperança apresentou um fragmento exclusivo. A diferenciação genética foi baixa e o número de migrantes por geração foi alto entre os estoques de reprodutores. O dendrograma não separou os indivíduos dos estoques de reprodutores em grupos distintos. Há alta variabilidade genética nos estoques de reprodutores, um pouco inferior no estoque de Vale Verde, e há grande proximidade genética entre os indivíduos dos estoques de reprodutores.

The genetic diversity of tambaqui (Colossoma macropomum) broodstocks from two hatchery station in Rondônia State was studied by the RAPD marker. Ten primers were used to analyze 30 broodstocks samples from the hatchery stations of Boa Esperança and Vale Verde. The polymorphic fragments percentage and Shannon genetic diversity index were high in the two broodstocks. The Boa Esperança broodstock presented an exclusive fragment. The genetic differentiation was low and the number of migrants per generation was high among the broodstocks. The dendrogram did not separate the broodstocks individuals in different groups. The results indicate a high genetic variability in the broodstocks, being a little bit lower in the Vale Verde broodstock. Besides, there is a genetic proximity among the broodstocks.